An Experimental and Analytical Study of the Fatigue Life of Weldments with Longitudinal Attachments 2001-01-0085
Both the experimental results and the analytical predictions of this study confirm that the poor fatigue performance of weldments with longitudinal attachments is due to poor weld quality which in turn leads to either a cold-lap or a very small weld toe radius. as well as to the combination of a very high 3-D stress concentration, and very high tensile residual stresses. Consequently, a specially designed stress-concentration-reducing part termed “stress diffuser” incorporated in the wrap-around welds at the ends of the longitudinal attachments increased the fatigue strength of longitudinal attachments to equal that of transverse attachments but only when cold-laps were eliminated.
The fatigue life predictions made using the a two-stage Initiation-Propagation (IP) Model were in good agreement with the experimental results. Procedures for correcting for the curved shape of the crack path are investigated. Cold-lap defects were predicted to eliminate the fatigue crack initiation life but to affect very little the fatigue crack propagation life.
Citation: Dimitrakis, S. and Lawrence, F., "An Experimental and Analytical Study of the Fatigue Life of Weldments with Longitudinal Attachments," SAE Technical Paper 2001-01-0085, 2001, https://doi.org/10.4271/2001-01-0085. Download Citation
Author(s):
S. D. Dimitrakis, F. V. Lawrence
Affiliated:
Parsons Brinckerhoff, Inc., University of Illinois at Urbana-Champaign
Pages: 14
Event:
SAE 2001 World Congress
ISSN:
0148-7191
e-ISSN:
2688-3627
Also in:
Fatigue and Failure of Spot Welds and Weld Joints-SP-1621, SAE 2001 Transactions Journal of Materials & Manufacturing-V110-5
Related Topics:
Fatigue
Tensile strength
Welding
SAE MOBILUS
Subscribers can view annotate, and download all of SAE's content.
Learn More »