Optimisation of Nocolok(TM) Brazing Conditions for Higher Strength Brazing Sheet

R. K. Bolingbroke; A. Gray; D. Lauzon

doi:10.4271/971861

1997-05-19

Optimisation of Nocolok(TM) Brazing Conditions for Higher Strength Brazing Sheet 971861

In non-corrosive flux brazing the flux contains a eutectic mixture of K₃AIF₆, and KAIF₄, which starts to melt at around 560°C. The melted flux disrupts the existing oxide film on aluminium alloys and suppresses further oxidation thus maintaining fluidity of the AI-Si based brazing alloy.

To facilitate downgauging there is a drive to develop higher strength core alloys. Using alloys with an increased level of magnesium will readily achieve significant improvements in post-brazed strength, however, the brazeability of alloys containing high levels of magnesium deteriorates as a result of magnesium reacting with the flux to form a higher melting point compound, which inhibits fluidity of the molten cladding alloy.

This paper discusses the influence of brazing conditions to increase tolerance to magnesium in core alloys. Once the optimum brazing conditions are established for varying levels of magnesium, the use of high strength magnesium containing alloys can be exploited for specific components, eg side supports and headers.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Digital $37.00 Print $37.00

Preview Document

We also recommend:

Standards

SAE Mobilus®

Publications

News

Events

Professional Development

A World in Motion (PreK-12)

Participate with SAE

SAE Membership

Donate

Optimisation of Nocolok(TM) Brazing Conditions for Higher Strength Brazing Sheet 971861

SAE MOBILUS